| Composition: blend of cement and sand as well as mineral admixtures, additives and fibres | |
| Bulk density | approx. 1.4 kg/dm³ |
| Appropriate amount of water | approx. 6,75 dm³/25 kg |
| Initial adhesion | ≥ 1.0 MPa |
| Adhesion after immersion in water | ≥ 1.0 MPa |
| Adhesion after thermal ageing | ≥ 1.0 MPa |
| Adhesion after freezing cycles | ≥ 1.0 MPa |
| Open time | ≤ 30 minutes |
| Slip | ≤ 0.5 mm |
| Adjustment time | ≤ 10 min |
| Workability | approx. 2 h from mixing with water |
| Adhesive layer thickness | 2-8 mm |
| Stepping on tiles and grouting after | after 24 h |
| Usable after: – foot traffic – full foot traffic load – spaces with heating |
3 days 7 days 21 days |
| Fire resistance | class A2-s1, d0/A2fl-s1 |
| Yield per bag | approx. 11 m² out of 25 kg |
| Approximate coverage of dry mix for fixing 1 m² of tiles using a rectangular notch trowel with the following size: 4×4 mm 6×6 mm 8×8 mm 10×10 mm |
approx. 1.7 kg approx. 2.3 kg approx. 2.6 kg approx. 2.9 kg |
For bonding of ceramic tiles (porcelain, glazed, terracotta, stoneware, clinker tiles), stone (insensitive to discolouration), concrete, cement, ceramic mosaic (excluding glass transparent and discolouring/dyeing-sensitive mosaics), as well as other tiles of different sizes, including large format tiles. Recommended for use on standard (non-deformable) and critical (deformable, heated, terraces and balconies) substrates. In case of fixing stone cladding, it is necessary each time to test material resistance to discolouration each time. Intended for interior and exterior use.
Examples of work sites
Residential buildings. Traffic routes and places with low and medium operating loads in public utilities, service and commercial facilities, health care, offices, schools, hotels, stations, exhibition halls, etc. Dry places and places exposed to water and moisture inside buildings (e.g. bathrooms, showers, kitchens) and outside (plinths, walkways, arcades and gates). Surfaces with heating (under-floor/wall). Balconies, terraces, loggias.